Alkaline water electrolysis has a long history in the chemical industry. It is a type of electrolyzer that is characterized by having two electrodes operating in a liquid alkaline electrolyte solution of potassium hydroxide (KOH) or sodium hydroxide (NaOH). These electrodes are separated by a diaphragm, separating the product gases and transporting the hydroxide ions (OH-) from one electrode to the other. A recent comparison showed that state-of-the-art nickel based water electrolyzers with alkaline electrolytes lead to competitive or even better efficiencies than acidic polymer electrolyte membrane water electrolysis with platinum group metal based electrocatalysts.
Electrolysis requires minerals to be present in solution. Tap, well, and ground water contains various minerals, some of which are alkaline while others are acidic. Water above a pH of 7.0 is considered alkaline; below 7.0 it is acidic. Electrolysis can occur only if the water is acidic or alkaline. The requirement is that there must be ions in the water to conduct electricity for the water electrolysis process to occur.
Video Alkaline water electrolysis
Technical Details
The electrodes are typically separated by a thin porous foil (with a thickness between 0.050 to 0.5 mm), commonly referred to as diaphragm or separator. The diaphragm is non-conductive to electrons, thus avoiding electrical shorts between the electrodes while allowing small distances between the electrodes. The ionic conductivity is supplied by the aqueous alkaline solution, which penetrates in the pores of the porous diaphragm. The state-of-the-art diaphragm is Zirfon, a composite material of zirconia and Polysulfone. The diaphragm further avoids the mixing of the produced hydrogen and oxygen at the cathode and anode, respectively. Typically, Nickel based metals are used as the electrodes for alkaline water electrolysis. Considering pure metals, Ni is the most active non-noble metal . The high price of good noble metal electrocatalysts such as platinum group metals and their dissolution during the oxygen evolution is a drawback. Ni is considered as more stable during the oxygen evolution.
High surface area Ni catalysts can be achieved by dealloying of Nickel-Zinc or Nickel-Aluminium alloys in alkaline solution, commonly referred to as Raney Nickel. In cell tests the best performing electrodes thus far reported consisted of plasma vacuum sprayed Ni alloys on Ni meshes and hot dip galvanized Ni meshes . The latter approach might be interesting for large scale industrial manufacturing as it is cheap and easily scalable.
Maps Alkaline water electrolysis
Advantages compared to PEM water electrolysis
In comparison to polymer electrolyte water electrolysis, another established technology to conduct low temperature water electrolysis, advantages of alkaline water electrolysis are mainly: (1) Cheaper catalysts compared to the platinum metal group based catalysts used for PEM water electrolysis. (2) Higher durability due to an exchangeable electrolyte and lower dissolution of anodic catalyst. (3) Higher gas purities due to lower gas diffusivity in alkaline electrolyte.